• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

  • Article Code : NWSA-7795-3400
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0086
  • Page Number : 22-30
  • Doi : 10.12739/NWSA.2014.9.3.2A0086
  • Abstract Reading : 1409
  • Download : 151
  • Share :

  • PDF Download

Issue Details

  • Year : 2014
  • Volume : 9
  • Issue : 3
  • Number of Articles Published : 2
  • Published Date : 1.07.2014

Cover Download Context Page Download
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

AISI 420 MARTENZİTİK PASLANMAZ ÇELİĞİN SÜRTÜNME KAYNAK YÖNTEMİ İLE BİRLEŞTİRİLEBİLİRLİĞİNİN ARAŞTIRILMASI

Nida KATI 1 , Sermin OZAN 2

Bu çalışmada, ergitme kaynak yöntemleri ile birleştirilmesi güç olan martenzitik paslanmaz çelik (AISI 420) sürtünme kaynak yöntemi ile birleştirilmiştir. Kaynak esnasında üç farklı devir kullanılmış ve sürtünme basıncı, sürtünme süresi, yığma süresi ve yığma basıncı gibi parametreler sabit tutulmuştur. Kaynak işleminden sonra, kaynak arayüzeyleri SEM ile incelenmiştir. Daha sonra bu parçalar mikrosertlik testine tabi tutulmuştur. Kaynaklı bağlantıların mekanik dayanımlarının belirlenmesi için kaynaklı parçalar çekme testine tabi tutulmuştur. İncelemelerin sonunda, AISI 420 martenzitik paslanmaz çeliğin sürtünme kaynak yöntemi ile problemsiz bir şekilde kaynak edilebildiği gözlemlenmiştir.

Keywords
Martenzitik paslanmaz çelik, AISI 420, Sürtünme Kaynağı, Mikroyapı, Mekanik Özellikler,

INVESTIGATION OF JOINABILITY BY FRICTION WELDING METHOD OF AISI 420 MARTENSITIC STAINLESS STEEL

Nida KATI 1 , Sermin OZAN 2

In thıs study, martesitic stainless steel (AISI 420) that is difficult to bond by fusion welding methods joined by friction welding. During welding, three different rotational speeds were used and parameters such as friction pressure, friction time, forging pressure and forging time were kept constant. After the welding process, welding interfaces were examined by SEM. Then these parts were subjected to microhardness test. Welded parts were subjected to tension test for determine the mechanical strength of welded joints. After investigations, AISI 420 martesitic stainless steel were observed that without a problem can be welded by friction welding.

Keywords
Martensitic stainless steel, AISI 420, Friction Welding, Microstructure, Mechanical Properties,

Details
   

Authors

Nida KATI (1) (Corresponding Author)

Fırat Üniversitesi
nkati@firat.edu.tr

Sermin OZAN (2)

Fırat Üniversitesi
serozan@firat.edu.tr

Supporting Institution

:

Project Number

:

Thanks

:
References