• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-2422-3963
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0453
  • Page Number : 89-99
  • Doi : 10.12739/NWSA.2020.15.2.1A0453
  • Abstract Reading : 548
  • Download : 124
  • Share :

  • PDF Download

Issue Details

  • Year : 2020
  • Volume : 15
  • Issue : 2
  • Number of Articles Published : 5
  • Published Date : 1.04.2020

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

PASLANMAZ ÇELİK İLE DÜŞÜK KARBONLU ÇELİK MALZEMELERİN MIG KAYNAK YÖNTEMİYLE BİRLEŞTİRİLEBİLİRLİĞİNİN İNCELENMESİ

Yakup KAYA1 , GÖKHAN ÇAYIRHAN2 , Mehmet BÖKÜ3 , Nizamettin KAHRAMAN 4

Bu çalışmada, 3 mm kalınlıkta paslanmaz çelik ve düşük karbonlu çelik levhalar; MIG kaynak yöntemi ile farklı parametreler kullanarak birleştirilmiştir. Birleştirilen numunelere çekme, eğme, çentik darbe testleri uygulanmış ayrıca mikrosertlik ve mikroyapı özellikleri incelenmiştir. Çekme testleri sonucunda; malzemelerin kaynak metali veya ısı tesiri altında kalan bölgeden (ITAB) ayrılmadığı, kopmanın düşük karbonlu çelik malzemede meydana geldiği tespit edilmiştir. Eğme testlerinde; kaynaklı numuneler 180° eğildiklerinde gözle görülebilir bir kaynak hatasına rastlanılmamıştır. Çentik darbe testlerinde, kaynak metali darbe tokluğu ITAB’lardan daha yüksek ölçülmüştür. Mikrosertlik testleri sonucunda en yüksek sertlik değeri kaynak metalinde ölçülmüştür. Mikroyapı incelemelerinde ısı girdisine bağlı olarak, paslanmaz çelik ve düşük karbonlu çeliğin ITAB bölgesinde tane irileşmesinin meydana geldiği tespit edilmiştir.

Keywords
MIG Kaynağı, Paslanmaz Çelik, Düşük Karbonlu Çelik, Mekanik Özellikle, Mikroyapı,

AN INVESTIGATION OF JOINABILITY OF STAINLESS STEEL AND THE LOW CARBON STEEL MATERIALS BY MIG WELDING METHOD

Yakup KAYA1 , GÖKHAN ÇAYIRHAN2 , Mehmet BÖKÜ3 , Nizamettin KAHRAMAN 4

In this study, stainless steel and low carbon steel plates with 3 mm thickness were joined using different parameters by MIG welding method. Tensile, bending, notch impact tests were applied to the joined samples and microhardness and microstructure properties were examined. The results of the tensile test indicated that separation was not occurred on weld metal or heat affected zone (HAZ). In that case fracture observed at low carbon steel side in the all samples. No crack or separation was observed in welded samples during 180° bending tests. In notched impact tests, weld metal impact strength is measured higher than HAZ. As a result of microhardness tests, the highest hardness is measured in the weld metal. In microstructure investigation, the grain growth was observed in the HAZ of the stainless steel and low carbon steel depending on the exerted heat input.

Keywords
MIG welding, Stainless Steel, Low Carbon Steel, Mechanical Properties, Microstructure,

Details
   

Authors

Yakup KAYA (1) (Corresponding Author)
KARABÜK ÜNIVERSITESI
ykaya@karabuk.edu.tr | 0000-0002-9951-2844

GÖKHAN ÇAYIRHAN (2)

YTU ÇELİK
gkhncyrhn@gmail.com | 0000-0001-7400-4379

Mehmet BÖKÜ (3)

mhmtbk.92@gmail.com | 0000-0003-1865-9017

Nizamettin KAHRAMAN (4)

Karabük Üniversitesi
nizamettinkahraman@hotmail.com

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Kaya, Y., (2010). AISI 304 ve AISI 430 Paslanmaz Çeliklerin TIG, MIG ve Örtülü Elektrod Ark Kaynağıyla Birleştirilebilirliğinin Araştırılması. Gazi Üniversitesi Mühendislik- Mimarlık Fakültesi Dergisi, 25(3):549-557.